Material Specifications:
ABS 94 VO: CHI MEI POLYAC ABS PA-765 UL FILE #: E56070
| PROPERTY | METHOD | UNIT | ABS 94VO |
| PHYSICAL | |||
| Melt Flow Index 200°C x 5 kg (cond. G) | ASTM D1238 | g/10 min | 5.2 |
| 230°C x 3.8 kg (cond. I) | ASTM D1238 | g/10 min | 13 |
| 220°C x 10 kg | ISO 1133 | g/10 min | 60 |
| Specific Gravity | ASTM D792 | ------------ | 1.20 |
| Mold Shrinkage (Flow, 1/8 in) | ASTM D955 | in/in x 10-3 | 3-7 |
|
MECHANICAL @73°C |
|||
| Izod Impact Strength (Notched) 1/8” | ASTM D256 | ft • lb/in (J/m) | 3.7 (198) |
| Izod Impact Strength (Notched) 1/4” | ASTM D256 | ft • lb/in (J/m) | 2.9 (155) |
| Tensile Strength at Yield | ASTM D638 | psi Mpa |
5500 38 |
| Tensile Modulus (6mm/min) | ASTM D638 | psi Mpa |
360000 2482 |
| Elongation at Break | ASTM D638 | % | 15 |
| Flexural Modulus | ASTM D790 | psi Mpa |
300000 2068 |
| Flexural Strength at Yield | ASTM D790 | psi Mpa |
8800 61 |
| Hardness (Rockwell, R-Scale) | ASTM D785 | ----------- | 100 |
| THERMAL | |||
| Heat Deflection Temp. (1/4” Test Specimens) | ASTM D648 | ||
| 264 psi (1.82 Mpa) Unannealed | °F(°C) | 163 (73) | |
| 264 psi (1.82 Mpa) Annealed | °F(°C) | 181 (83) | |
| 66 psi (0.46 Mpa) Unannealed | °F(°C) | 181 (83) | |
| Vicat Softening Temp (1kg, 50°C/hr) | ASTM D1525 | °F(°C) | 194 (90) |
| Coefficient of Thermal Expansion | ASTM D696 | in/in/°F x 10-5 | 7.2 |
| (-40°C → 80°C, Annealed) | mm/mm/°F x 10-5 | 12.9 | |
| ELECTRICAL @73°F | |||
| Volume Resistivity | ASTM D257 | ohm-cm | > 1015 |
| FLAME CLASS RATING | |||
|
UL 94VO (Min. Tested Thickness) |
UL94 | in (mm) | 0.062 (1.57) |