EI 100, M6 29 Gauge Orientated Single Phase Steel Lamination (1 string).

filler

Price:
Sale price$158.60

Shipping calculated at checkout

NOTE: Only ships to U.S. and Canada.

Description

General Information
M6 29 Gauge - 0.014" (0.355 mm) Grain Orientated Electrical Transformer Steel Lamination, RoHS compliant. This steel is used in audio amplifiers, current, output, power transformers; chokes and saturable reactors; and ferro-resonant regulators. The squared hysteresis loop iron-silicon alloy was expressly developed to provide lower core loss with higher permeability in the rolling direction. Grain oriented laminations are supplied in the stress relief annealed condition. The elementary patterns of the crystals in the material are "oriented", or so arranged that the axis of easiest magnetization is nearly parallel and aligned in the direction of rolling. The alignment is accomplished by special cold-rolling and annealing processes. This allows the product to withstand more severe vibration and shock and enables the following:

  1. Lower core losses as a consequence of design.

  2. Higher initial permeability.

  3. Higher permeability at higher inductions.

  4. More stable VA/Temperature relationship over a wide range of ambient temperatures.
Strings ≅ Weight (lbs.) ≅ Weight (Kg) ≅ "EI" Sets
1 14.77
6.7
660


Specifications

Dimensional Drawing 20000-EI100
Thickness Lamination Weight
in. mm lb./1000 pcs Kg/1000 pcs "EI"s/lb. "EI"s/Kg
0.014 0.355 22.351
10.138
44.7
98.6

 

Characteristics of a Square Core Stack 

Window Dimensions 1.500 in. x 0.500 in. 0.750 in.2 4.839 cm.2
Volume, Solid 5.850 in.3 95.859 cm.3
Cross Section Area, Solid 1.000 in.2 6.452 cm.2
Sets 71
Weight 1.587 lbs. 0.720 Kg
Length of Magnetic Path 6.000 in. 15.240 cm.
Specific Gravity - Grams per cu. cm. (A.S.T.M.) 7.65
Vol. Resistively - Microhms per cm. cube 45
Saturation Induction (Gauss) 20,300
Max. aging - Core Loss % 5
Coercive Force - (Oersteds) Annealed 0.12
Hysteresis Loss at 10 Kilogauss (Ergs/cycle/cm.3) 260

 

Typical D.C. Permeability Value (Max)

100 Gauss 6,000
1,000 Guass 17,000
10,000 Guass 50,000
16,000 Guass 47,000

 

Design Formulas

BMAX = (58.1 x 103) / K1N = Gauss per volt
HO = (0.082 x 10-3) = Oersteds per milliampere of direct current
La = (0.56 x 10-8) K1 N2 μAC = Henrys

60 Hz. Reactance (N = number of turns)

EDCOR sells steel laminations from Tempel Steel and Thomas & Skinner. For more information on the specifications please visit the companies websites: www.tempel.com  and thomas-skinner.com.

Payment & Security

American Express Apple Pay Diners Club Discover Meta Pay Google Pay Mastercard PayPal Shop Pay Venmo Visa

Your payment information is processed securely. We do not store credit card details nor have access to your credit card information.

You may also like

Recently viewed